石英玻璃管尺寸技术公差参数2010/05/12
具体的尺寸公差和技术指标请参见所附的表Ⅰ，表Ⅱ，表Ⅲ，表Ⅳ，表V。
| 典型尺寸，透明熔凝石英管 Stapdard sizes for clear fused quartz tubes |
|
|
|
| 尺寸公差 Dimensional Tolerance(table Ⅱ) |
|
外径范围
Range of OD |
外径
OD |
壁 厚
WT |
偏壁度
Siding |
椭圆度
Ellipsticity |
弯曲度
Camber/1220mm |
|
≤5mm
|
±2.0%
|
±10%
|
12%
|
2.0%
|
2.5mm
|
|
6.00-15.00mm
|
±1.25%
|
±8%
|
10%
|
1.5%
|
2.5mm
|
|
15.00-20.00mm
|
±1.25%
|
±10%
|
15%
|
1.5%
|
2.5mm
|
|
20.00-25.00mm
|
±1.25%
|
±10%
|
15%
|
1.5%
|
3.0mm
|
|
25.00-30.00mm
|
±1.35%
|
±12%
|
15%
|
1.5%
|
3.0mm
|
|
30.00-80.00mm
|
±1.5%
|
±14%
|
15%
|
2.0%
|
3.0mm
|
| 化学成份 Chemical Composition 单位 unit: ppm(tableⅢ) |
|
铬Cr
|
锗Ge
|
铁Fe
|
镁Mg
|
钛Ti
|
钙Ca
|
铝Al
|
钠Na
|
锂Li
|
钾K
|
|
0.1
|
0.4
|
1.5
|
0.4
|
0.1
|
0.8
|
14
|
2.3
|
0.5
|
2.0
|
| 光在1.0mm厚处的透过率 Lights transmittance(table Ⅳ) |
| nm | ≤220 | 255 | 280 | 315 | 350 | 380 | 590 | 780 |
| % | 89 | 91 | 93 | 93 | 93 | 93 | 93.2 | 93.4 |
| 物理性能 Physical capability(table V) |
| 214 | 219 | 254 | |
| 密度（g/cc） | 2.2 | 2.21 | 2.21 |
| 热膨胀系数（cm/cm℃） | 5.5×10-7 | 5.9×10-7 | 6.7×10-7 |
| 软化点(℃) | 1683 | 1660 | 1615 |
| 退火点(℃) | 1215 | 1204 | 1163 |
| 变形点(℃) | 1120 | 1106 | 1066 |
| 折射率 | 1.4585 | 1.456 | 1.460 |
| 比热（j/kg0k） | 670 | 700 | 690 |
| 抗压强度(Pa) | ＞1.1×109 | 0.94×1109 | 0.55×109 |
| 杨氏模量(Pa) | 7.2×1010 | 7.5×1010 | 7×1010 |
| 电阻率（ohm cm@350℃） | 7×109 | 2.5×1010 | 5×1010 |
| 介电常数（@1MHz） | 3.75 | 5.8 | 6 |